Thermosetting ink for touch screen application
Resist ink with flexibility and adhesion. Regardless of resistive touch screen or capacitive touch screen,
it has good usage record as overcoat material.
| Products |
Outline |
Color |
Total
Transmittance |
Haze |
Viscosity
(at 25℃)
(VT-06)
|
Curing
condition |
| CR-18T-KT1 |
2 component type,
Thick film coating
is possible |
Milky white |
≧90% |
≧70% |
40-70 dPa･s |
130℃×10min |
Themosetting High Transparency ink for touch screen application
Excellent transparency, not only suitable for use as frame circuit protection, but also in application to view area.
| Products |
Outline |
Color |
Total
Transmittance |
Haze |
Viscosity
(at 25℃) |
Curing
condition |
| FR-1T-NSD9 |
2 component type,
High transparency,
High smoothness |
Slightly muddy,
transparent |
≧99% |
Approx. 0.2% |
20-60 dPa･s
(B-8U)
|
110℃×30min |
| FR-410T-NF2 |
2 component type,
High transparency,
High chemical resistance. |
Slightly muddy,
transparent |
≧99% |
Approx. 0.2% |
150-250 dPa・s
(VT-06) |
130℃x30min |
UV curing type ink for touch screen application
It has good usage record as overcoat for touch screen that cannot be subjected to heat, and as Dot-spacer for resistive touch screen.
| Products |
Outline |
Color |
Viscosity
(at 25℃)
(VT-06) |
UV Exposure |
| UVF-10T-DS |
1 component type,
For Dot-spacer application,
Fine pattern, Thick film |
Milky white |
900-1300 dPa・s |
≧ 1000 mJ/cm2 |
| UVF-DS3 |
1 component type,
For Dot-spacer application,
High strength |
Milky white |
750-950 dPa・s |
≧ 600 mJ/cm2 |
| UVF-10T(KAI) |
1 component type,
General-purpose |
Milky white |
100-200 dPa・s |
≧ 800 mJ/cm2 |
| UVF-31T |
1 component type,
High adhesion |
Milky white |
400-600 dPa・s |
≧ 800 mJ/cm2 |
| UVF-70T |
1 component type,
High adhesion.
|
Slightly turbid transparent |
500-2500 mPa・s |
≧ 1000 mJ/cm2 |
UV curing High Transparency ink for touch screen application
High anti-sulphurization effect as protective coating of Ag curcuit makes it suitable for automotive application.
| Products |
Outline |
Color |
Total
Transmittance |
Haze |
Viscosity
(at 25℃)
(B-8U)
|
Curing
condition |
| UVR-100 |
1 component type,
High transparency,
Good sulfurization resistance,
Thermal dry+UV curing type |
Light yellow,
transparent |
≧100% |
Approx. 0.3% |
1000-3000
mPa･s |
80℃×30min
→1000mJ/cm2 |
| UVR-200(611) |
1 component type,
High transparency,
Good sulfurization resistance |
Light yellow,
transparent |
≧99% |
Approx. 0.5% |
1000-5000
mPa・s |
1000mJ/cm2 |
Black ink with High Hiding performance for touch screen application
Frame decoration, concealment application for touch panels, for circuit concealment.
| Products |
Outline |
Surface
condition |
Total
Transmittance |
Viscosity
(at 25℃) |
Curing
condition |
| FR-231C-2 |
2 component type,
High hiding performance,
High adhesion |
Without gloss |
0.00% |
100-200 dPa・s
(VT-06)
|
100℃ x 20min |
Over coat ink for vacuum forming
For curved surface 3D of sensors such as touch panel.
| Products |
Outline |
Color |
Stretching property |
Viscosity
(at 25℃)
(VT-06)
|
Curing
condition |
| CR-80T-11 |
1 component type,
Thermal dry type |
Milky white |
120% |
250-350 dPa・s |
100℃ x 30min |